Resin Property | Method | Condition | Unit | Value |
Melt Index | ASTM D1238 | 190℃/2.16kg | g/10min | 18 |
Density | ASTM D1505 | 23℃ | g/? | 0.960 |
Melt Temperature | ASTM D3418 | 10℃/min | ℃ | 62 |
Vicat softening point | ASTM D1525 | - | ℃ | <40 |
Ultimate tensile | ASTM D638 | 500mm/min | kgf/? | 100 |
Ultimate elongation | ASTM D638 | 500mm/min | % | 900 |
乙烯乙酸含量 | 特点 |
10% | 比聚乙烯柔软,耐冲击强度好,用作包装袋和薄膜以及注射模塑件,电缆覆层、玩具等 |
10%-20% | 透明性良好,耐寒耐应力开裂,用于制农业薄膜,医疗用具等 |
20%-40% | 具有良好的黏合性,用作热熔胶黏剂、涂料等 |
45%-55% | 弹性良好,用作特种橡胶,与其他橡胶相容性好,加工性也好,可用过氧化物硫化,与硫化橡胶不相上下 |
65%~95% | 为乳液,可用作纤维、纸张等的胶黏剂 |